耐磨陶瓷涂层HC3010

耐磨陶瓷涂层HC3010

日期:2022-03-03 人气:1396
耐磨陶瓷涂层HC3010


使用方法:Usage method
1
、表面处理:对待修复部位进行粗化处理(角磨机打磨或喷砂等),然后用专用清洗剂清洗并晾干;处理过的基材表面应该粗糙、干净、干燥;


Surface treatment: The parts to be repaired shall be roughened (angle grinder grinding or sand blasting, etc.), then cleaned with special cleaning agent and dried; The treated substrate surface shall be rough, clean and dry
2
、配制:将AB组份按比例混合均匀,并在30min内用完。


Preparation: Mix the AB Components evenly in proportion and use them up within 30mins


  1. 涂敷:本产品合适的涂层厚度是38mm,最厚可涂30mm,应将混合好的材料逐层涂敷于待修部位,第一层要压实,使之与基材充分浸润;涂层涂到尺寸后表层要修平整,本材料不能进行机械加工,应注意控制涂层厚度,以免装配中出现干涩现象。

    Coating: The appropriate coating thickness of this product is 3-8mm, and the maximum thickness can be 30mm. The mixed materials shall be applied to the parts to be repaired layer by layer. The first layer shall be compacted to make it fully wet with the base material; After the coating is applied to the required thickness, the surface layer shall be leveled. This material cannot be machined. The coating thickness shall be controlled to avoid dryness during assembly
    4
    、固化:25℃固化24小时可投入使用(如能加热到80℃保温2小时,可提高综合性能的30%),若温度低于5℃应采用加热或延长固化时间来促进固化。一般冬天施工可用碘钨灯距涂层40cm的距离进行照射加温。

    Curing: Curing at 25 for 24 hours can be put into use (if the temperature can be heated to 80 for 2 hours, the comprehensive performance can be improved by 30%). If the temperature is lower than 5 , heating or extending the curing time should be used to promote curing. In general, iodine tungsten lamp can be used to irradiate and heat the coating at a distance of 40cm in winter

    注意事项:Notes

    胶液一般是边施工边配置,一次配制量最大不能超过4公斤,过多胶凝固的过快,还没用完已经部分凝固而不能使用。可根据实际温度冬天适当多配,夏天适当少配。如气温过低可将A组份适当加热以降低粘度便于配置。

    The product is generally prepared during construction. The maximum amount of product prepared at one time should not exceed 4kg. Too much amount solidifies too fast and cannot be used until it has been partially solidified. According to the actual temperature, it can be more in winter and less in summer. If the temperature is too low, A Component can be heated appropriately to reduce the viscosity and facilitate configuration.



项目Item/指标Index

Wearing compound ceramic bead filled epoxy耐磨陶瓷颗粒胶

品名Series

HC3010

颜色color

褐色Brown

密度Densityg/cm3

2.25

重量配比Weight ratioA:B

2:1/3:1

体积配比 Volume ratioA:B

2:1/3:1

操作时间

Operation time (200g mixing, min)

30

完全固化时间Full curing timeh

24

固化后硬度After curing hardness(ShoreD)GB/T2411-2008

89.0

抗压强度Compressive strength(MPa) GB/T1041-2008

110.0

拉伸强度Tensile strength(MPa) GB/T6329-1996

28.0

剪切强度Shear strength(MPa) GB/T7124-2008

16.0

工作温度Working temperature(℃)

-60120

保质期Expiration dateyears

2