产品特点：Product features
双组份，粘接强度高，立面不流淌
Two component, high adhesive strength, no flow on the facade
广泛应用于-60℃-200℃工况的耐磨陶瓷片与金属的粘接。
Widely used in the bonding of wear-resistant ceramic sheet and metal under - 60 ℃ - 200 ℃
注意事项：Note
-
每次配胶不宜过多，配胶后应尽快用完。
Do not mix too much each time, and use it up as soon as possible after mixing
-
胶液凝胶时间与温度有关，温度越高，凝胶越快。
The solidification time is related to the temperature. The higher the temperature, the faster the solidification
使用方法：Usage method
-
表面处理：除去待粘表面锈迹灰尘、油污等，并用清洁剂清洗干净。
Surface treatment: Remove rust, dust, oil stain, etc. on the surface to be adhered, and clean it with detergent
-
配制：按A:B=4:1(重量比)混合并搅拌均匀。
Preparation: Mix according to A: B = 4:1 (weight ratio) and stir evenly
-
涂敷：将调匀后的胶涂于已处理干净的待粘表面，然后将两接触面合拢并施加接触压力。8-10小时可基本达到结构强度，可随温度的升高而进一步固化。
Coating: Apply the mixed glue to the cleaned surface to be adhered, then close the two contact surfaces and apply contact pressure. The structural strength can be basically reached in 8-10 hours, and it can be further cured with the increase of temperature
-
固化：室温24小时或者80℃保持3小时固化完全。
Curing: 24 hours at room temperature or 3 hours at 80 ° C
|
项目Item/指标Index |
耐磨陶瓷胶Wear-resistant ceramic adhesive |
||
|
品名Series |
HC6868 |
HC0868 |
HC8410 |
|
颜色color |
白色White |
白色（浅黄） White (light yellow) |
灰色/白色Grey/White |
|
密度Density（g/cm3） |
1.28 |
1.66~1.70 |
1.48~1.52 |
|
重量配比Weight ratio（A:B） |
4:1 |
1:1 |
4:1 |
|
体积配比 Volume ratio（A:B） |
4:1 |
1:1 |
4:1 |
|
操作时间 Operation time (200g mixing, min) |
30 |
30 |
30 |
|
完全固化时间Full curing time（h） |
24 |
24 |
24 |
|
拉伸强度Tensile strength(MPa) GB/T6329-1996 |
65.0 |
65.0 |
35.0 |
|
剪切强度Shear strength(MPa) GB/T7124-2008 |
≥10 |
≥10 |
≥18 |
|
工作温度Working temperature（℃） |
-60-150 |
-60-150 |
-60-200 |
|
保质期Expiration date（years） |
2 |
2 |
2 |